7039 Aluminium Plate
The only high strength, wrought, 7000 series aluminum alloy with a military specification is the 7039 aluminum Plate, controlled by MIL-DTL-46063H(MR). Aluminium / aluminum 7039 Plate is a heat treatable wrought alloy. The 7075 Aluminium Plate is similar to 7039 aluminum armor plate, but with higher strength.
Sasa Aluminium is the leading manufacturer and exporter of 7039 Aluminium Plate. Supplier of ASTM B209 7039 Aluminium Plate from 0.5mm to 5mm Thick 1000mm x 1000mm to 2500mm x 1250mm Tempers manufactured in accordance with international standards ASTM B209, ASTM-B-209, EN573, and EN485, check 7039 Aluminium Plate price. The general widths of 7039 H16 Aluminum Plates are 1000mm, 1250mm and 1500mm, while common lengths are 2000mm, 2500 mm and 3000mm respectively. Wholesale Trader of 7039 Commercial Aluminium Plate offered by Sasa Aluminium , China. Stockist of 7039 Aluminium Plate, H32 7039 Aluminium Stucco Plate, H38 Commercial 7039 Aluminium Plate, ASME SB209 7039 Aluminium Patterned Plate, 7039 Mill Finish, 7039 Aluminium Extruded Plate, 7039 Aluminium Plate and 7039 Aluminium Plate in China.
| Standard Dimensions of 7039 Aluminium Plate: |
| Aluminium Alloy | ASTM B209 7039 |
| Aluminium 7039 Plate Temper | O, H12, H14, H16, H18, H22, H24, H26, H32, H112 |
| Aluminium 7039 Plate Thickness | 0.5mm-150mm |
| Aluminium 7039 Plate Width | 500-2000mm |
| Aluminium 7039 Plate Length | to clients’ requirement |
| Aluminium 7039 Plate Coating | Polyester, Fluorocarbon, polyurethane and epoxy coating |
| 7039 Aluminium Plate Coating finish | PVDF, POLYESTER(PE) |
| Aluminium 7039 Plate Surface | Polished, hair line, brush, sand blast, checkered, embossed, etching, etc. Mill finish, Bright finish, paper interleaved, one side film, both sides film. |
| Aluminium 7039 Plate Gloss | Meet the customer requirement |
| Total coating thickness of Aluminium 7039 Plate | PVDF coating: More than 25 micron; Polyester coating: More than 18 micron |
| Aluminium 7039 Plate Coating hardness | (pencil hardness) more than 2H |
| Aluminium 7039 Plate Coating adhesive | No lower than1st grade |
| Aluminium 7039 Plate Impact resistance | No cracking or peeling (50kg/cm, ASTMD-2794: 1993) |
| Aluminium 7039 Plate Flexibility (T-bend) | 2T |
| Aluminium 7039 Plate MEK resistance | More than 10 |
| Available Aluminium 7039 Plate Stock Sizes | 1ft x 1ft, 1ft x 2ft, 1ft x 4ft, 2ft x 2ft, 2ft x 4ft, 4ft x 4ft, 4ft x 8ft, 4ft x 10ft or Cut to Size or Custom Shape. |
| Aluminium 7039 Plate Delivery Time | 30-60 days after receiving the prepayment |
| Aluminium 7039 Plate Packaging Details | Standard export package. One pallet is about 2-3 ton.Two steel belts in width and three in width. One 20GP container can load about 18-20 tons Aluminium 7039 Plate. One 40GP container can load about 24 tons Aluminium 7039 Plate |
| ASTM B209 Alloy 7039 Plate Outer packing | Export standard, wooden pallet |
| Bottom side Aluminium 7039 Plate is coated with protective polyester material, thickness more than 6 micron | |
| We Export Aluminium 7039 Plate to | Singapore, Indonesia, Ukraine, Korea, Thailand, Vietnam, Saudi Arabia, Brazil, Spain, Canada, USA, Egypt, Iran, China, Kuwait, Dubai, Oman, Kuwait, Peru, Mexico, Iraq, Russia, Malaysia, etc. |
| Types of 7039 Aluminium Plate Manufacturer in China: |
| 7039 Aluminium Plates Product Range | ||||
|---|---|---|---|---|
| Alloy No. | Thickness (mm) |
Width (mm) |
Length (mm) |
Temper |
| 7039 Aluminium Plate | 0.2-5.0 | 20-2200 | 20-8000 | O, H12, H22, H14, H16, H18, H24, H26 |
| Standard Specification of 7039 Aluminium Plate: |
| China |
U.S.A. |
BRITAIN |
CANADA | GERMANY |
RUSSIA |
I.S.O. |
FRENCH | |
|---|---|---|---|---|---|---|---|---|
| New IS | Old IS | (A.A.) |
(B.S.) |
(DIN) | – | – | – | |
| 74530 | – | 7039 | – | D74S | – | – | 3004 | |
| 7039 Aluminium Plate Equivalent Grades |
| China |
U.S.A. |
BRITAIN |
CANADA | GERMANY |
RUSSIA |
I.S.O. |
FRENCH | |
|---|---|---|---|---|---|---|---|---|
| New IS | Old IS | (A.A.) |
(B.S.) |
(DIN) | – | – | – | |
| 74530 | – | 7039 | – | D74S | – | – | 3004 | |
| 7039 Aluminium Plate Sizes: |
| Sizes (mm) | Theoretical Mass KG/Plate |
|---|---|
| 2000 X 1000 X 0.5 | 2500 X 1250 X 0.5 |
| 2000 X 1000 X 0.7 | 2500 X 1250 X 0.7 |
| 2000 X 1000 X 0.9 | 2500 X 1250 X 0.9 |
| 2000 X 1000 X 1.2 | 2500 X 1250 X 1.2 |
| 3000 X 1500 X 1.2 | 2000 X 1000 X 1.6 |
| 2500 X 1250 X 1.6 | 3000 X 1500 X 1.6 |
| 2000 X 1000 X 2.0 | 2500 X 1250 X 2.0 |
| 3000 X 1500 X 2.0 | 2500 X 1250 X 2.5 |
| 2.79 | 4.36 |
| 3.91 | 6.10 |
| 5.02 | 7.85 |
| 6.74 | 10.46 |
| 15.01 | 8.93 |
| 13.95 | 20.09 |
| 11.16 | 17.44 |
| 25.11 | 21.80 |
| 7039 Aluminium Plate Weight Chart: |
Width: 1.000 mm | Length: 2.000 mm
| Product | Thickness | Weight |
|---|---|---|
| 7039 Aluminium Plate | 0,30 mm | 0,810 Kg/m2 |
| 7039 Aluminium Plate | 0,40 mm | 1,080 Kg/m2 |
| 7039 Aluminium Plate | 0,50 mm | 1,350 Kg/m2 |
| 7039 Aluminium Plate | 0,60 mm | 1,620 Kg/m2 |
| 7039 Aluminium Plate | 0,70 mm | 1,890 Kg/m2 |
| 7039 Aluminium Plate | 0,80 mm | 2,160 Kg/m2 |
| 7039 Aluminium Plate | 0,90 mm | 2,430 Kg/m2 |
| 7039 Aluminium Plate | 1,00 mm | 2,700 Kg/m2 |
| 7039 Aluminium Plate | 1,20 mm | 3,240 Kg/m2 |
| 7039 Aluminium Plate | 1,40 mm | 3,780 Kg/m2 |
| 7039 Aluminium Plate | 1,50 mm | 4,050 Kg/m2 |
| 7039 Aluminium Plate | 1,60 mm | 4,320 Kg/m2 |
| 7039 Aluminium Plate | 1,80 mm | 4,860 Kg/m2 |
| 7039 Aluminium Plate | 2,00 mm | 5,400 Kg/m2 |
| 7039 Aluminium Plate | 2,20 mm | 5,940 Kg/m2 |
| 7039 Aluminium Plate | 2,50 mm | 6,750 Kg/m2 |
| 7039 Aluminium Plate | 3,00 mm | 8,100 Kg/m2 |
| 7039 Aluminium Plate | 4,00 mm | 10,800 Kg/m2 |
| 7039 Aluminium Plate | 5,00 mm | 13,500 Kg/m2 |
| 7039 Aluminium Plate | 6,00 mm | 16,200 Kg/m2 |
| 7039 Aluminium Plate | 10,00 mm | 27,000 Kg/m2 |
| 7039 Aluminium Plate | 12,00 mm | 32,400 Kg/m2 |
| 7039 Aluminium Plate | 15,00 mm | 40,500 Kg/m2 |
| 7039 Aluminium Plate | 20,00 mm | 54,000 Kg/m2 |
| 7039 Aluminium Plate Chemical Composition: |
| Alloy (ISS) | Equivalent alloy (A.A) | Copper | Magnesium | Silicon | Iron | Managanese Others* (Total) | Remarks | ||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Old | New | U.S.A | Min. | Max. | Min. | Max. | Min. | Max. | Min. | Max. | Max | Max. | Aluminum 99.0% Min. | ||
| — | 74530 | 7039 | — | 0.2 | 1.0 | 1.5 | — | 0.4 | 0.7 | 0.2 | 0.7 | 0.4 | Zinc (5.1-6.1) & Chromium (0.2-0.28) | ||
| Aluminium 7039 Plate Mechanical Properties: |
| Properties | Metric | Imperial |
|---|---|---|
| Tensile strength (@diameter 12.7 mm/0.500 in) | 450 MPa | 65300 psi |
| Yield strength (@diameter 12.7 mm/0.500 in) | 380 MPa | 55100 psi |
| Elongation at break (@diameter 12.7 mm/0.500 in) | 13% | 13% |
| Elastic modulus | 69.6 GPa | 10100 ksi |
| Shear strength | 255 MPa | 37000 psi |
| Hardness, Brinell (@load 500 kg; thickness 10.0 mm/1100 lb;0.394 in) | 133 | 133 |
| Hardness, Knoop (converted from Brinell hardness value) | 167 | 167 |
| Hardness, Rockwell A (converted from Brinell hardness value) | 50 | 50 |
| Hardness, Rockwell B (converted from brinell hardness value) | 81 | 81 |
| Hardness, Vickers (converted from Brinell hardness value) | 153 | 153 |
Aluminum Alloy Heat Treatment Temper Designations
Basic Aluminum Heat Treatment Designations
- F As Fabricated
- O Annealed
- H Strain Hardened
- W Solution Heat Treated
- T Solution Heat Treated
Heat Treating T Temper Codes for Aluminium 7039 Plates
- T1 – Cooled from an elevated temperature shaping process and naturally aged to a substantially stable condition.
- T2 – Cooled from an elevated temperature shaping process, cold worked, and naturally aged to a substantially stable condition.
- T3 – Solution heat treated, cold worked, and naturally aged to a substantially stable condition.
- T4 – Solution heat treated, and naturally aged to a substantially stable condition.
- T5 – Cooled from an elevated temperature shaping process then artificially aged.
- T6 – Solution heat treated then artificially aged.
- T7 – Solution heat treated then overaged/stabilized.
- T8 – Solution heat treated, cold worked, then artificially aged.
- T9 – Solution heat treated, artificially aged, then cold worked.
- T10 – Cooled from an elevated temperature shaping process, cold worked, then artificially aged.
Additional digits may be used after the first T temper digit to indicate subsequent stress relieving by processes such as stretching, compressing, or a combination.
H Temper Strain Hardening Codes for Aluminium 7039 Plates
- H1 – Strain hardened only
- H2 – Strain hardened and partially annealed
- H3 – Strain hardened and stabilized
- H4 – Strain hardened and lacquered or painted. This assumes that thermal affects from the coating process affect the strain hardening; seldom encountered.
Application of 7039 Aluminium Plate
7039 Aluminium Plate is the most widely used form of Industrial Aluminium. 7039 Aluminium Plates find applications in various industries such as manufacturing cans and packages, transportation, home appliances, building and construction.