3003 H14 Aluminium Plate

Short Description:


Product Detail

FAQ

Product Tags

Aluminum 3003 H14 Plate is alloyed with 1.2% maganese to provide a tensile strength range of 17 to 30 KSI. 3003 H14 Aluminum Plate has Excellen workability, weldability, and corrosion resistance. Used for sheet metal work, fuel tanks, and other applications that require a slightly higher strength than 1100 series aluminum. Conforms to AMS QQ-A-250/2 and ASTM B209.

The 3003 h14 aluminum plate is a medium strength alloy that is made with 1.20 percent manganese. It is 20 percent stronger than 1100 series aluminum, which is why it’s a preferred metal and used for various applications in different industries. It has great resistance to corrosion, can be welded easily and has excellent workability. Aluminum Plate 3003 H14 can be used for sheet metal works, spinning, drawing, fuel tanks, tapping, forming and a variety of other applications. As a 3003 alloy, H14 aluminum plates can be formed easily. Debossing or embossing an alloy of this temper can typically be done without cracking or straining the metal.

3003 H14 Aluminium Plate ASTM B209, ASTM-B-209, EN573, and EN485 international standards.
AMS 4006 Plate/ AMS 4008 H14 Plate, SAE -QQ-A-250/2 T0, SAE -QQ-A-250/2 TH14, 3003-F Aluminum Plate:  ASTM-B-209

Sasa Aluminium Incorporation is the leading manufacturer and exporter of 3003 H14 Aluminium Plate. Supplier of ASTM B209 3003 H14 Aluminium Plate from 0.5mm to 5mm Thick 1000mm x 1000mm to 2500mm x 1250mm Tempers manufactured in accordance with international standards ASTM B209, ASTM-B-209, EN573, and EN485, check 3003 H14 Aluminium Plate price. The general widths of 3003 H14 H16 Aluminum Plates are 1000mm, 1250mm and 1500mm, while common lengths are 2000mm, 2500 mm and 3000mm respectively. Wholesale Trader of 3003 H14 Commercial Aluminium Plate offered by Sasa Aluminium Overseas, China. Stockist of 3003 H14 Aluminium Plate, H32 3003 H14 Aluminium Stucco Plate, H38 Commercial 3003 H14 Aluminium Plate, ASME SB209 3003 H14 Aluminium Patterned Plate, 3003 H14 Mill Finish, 3003 H14 Aluminium Extruded Plate, 3003 H14 Aluminium Plate and 3003 H14 Aluminium Plate in China.

3003 H14 Aluminium Plate Suppliers in UNS A93003 H14 Aluminium Plate stockist in China, 3003 H14 Aluminium Corrugated Plate Suppliers in Best Price of EN AW 3003 H14 H14 Aluminium Plate

You may intrested in:

  • 3003 H14 Aluminium Chequered Plate
  • 3003 H14 Aluminium Checker Plate
  • 3003 H14 Aluminium Diamond Plate
  • 3003 H14 Aluminium Tread Plate

 

Standard Dimensions of 3003 H14 Aluminium Plate

Standard dimensions (a x b) of Aluminium 3003 H14 Plate

Aluminium 3003 H14 Plate up to 9.9 mm
2.000 x 1.000 mm
2.500 x 1.250 mm
3.000 x 1.500 mm

Oversize Aluminium 3003 H14 Plate
4.000 x 2.000 mm
6.000 x 2.500 mm
8.000 x 2.500 mm

Other dimensions on request

3003 H14 Aluminium Plate Suppliers in , 3003 H14 Aluminium Plate Supplier Singapore, Dealer & Distributor of All 3003 H14 Aluminium Alloy Plate Grades, Stockholder of 3003 H14 Aluminium Plate 1mm

Aluminium Alloy ASTM B209 3003 H14
Aluminium 3003 H14 Plate Temper O, H12, H14, H16, H18, H22, H24, H26, H32, H112
Aluminium 3003 H14 Plate Thickness 0.5mm-150mm
Aluminium 3003 H14 Plate Width 500-2000mm
Aluminium 3003 H14 Plate Length to clients’ requirement
Aluminium 3003 H14 Plate Coating Polyester, Fluorocarbon, polyurethane and epoxy coating
3003 H14 Aluminium Plate Coating finish PVDF, POLYESTER(PE)
Aluminium 3003 H14 Plate Surface Polished, hair line, brush, sand blast, checkered, embossed, etching, etc.
Mill finish, Bright finish, paper interleaved, one side film, both sides film.
Aluminium 3003 H14 Plate Gloss Meet the customer requirement
Total coating thickness of Aluminium 3003 H14 Plate PVDF coating: More than 25 micron; Polyester coating: More than 18 micron
Aluminium 3003 H14 Plate Coating hardness (pencil hardness) more than 2H
Aluminium 3003 H14 Plate Coating adhesive No lower than1st grade
Aluminium 3003 H14 Plate Impact resistance No cracking or peeling (50kg/cm, ASTMD-2794: 1993)
Aluminium 3003 H14 Plate Flexibility (T-bend) 2T
Aluminium 3003 H14 Plate MEK resistance More than 10
Available Aluminium 3003 H14 Plate Stock Sizes 1ft x 1ft, 1ft x 2ft, 1ft x 4ft, 2ft x 2ft, 2ft x 4ft, 4ft x 4ft, 4ft x 8ft, 4ft x 10ft or Cut to Size or Custom Shape.
Aluminium 3003 H14 Plate Delivery Time 30-60 days after receiving the prepayment
Aluminium 3003 H14 Plate Packaging Details Standard export package.
One pallet is about 2-3 ton.Two steel belts in width and three in width.
One 20GP container can load about 18-20 tons Aluminium 3003 H14 Plate.
One 40GP container can load about 24 tons Aluminium 3003 H14 Plate
ASTM B209 Alloy 3003 H14 Plate Outer packing Export standard, wooden pallet
  Bottom side Aluminium 3003 H14 Plate is coated with protective polyester material, thickness more than 6 micron
We Export Aluminium 3003 H14 Plate to Singapore, Indonesia, Ukraine, Korea, Thailand, Vietnam, Saudi Arabia, Brazil, Spain, Canada, USA, Egypt, Iran, China, Kuwait, Dubai, Oman, Kuwait, Peru, Mexico, Iraq, Russia, Malaysia, etc.
AUTHORIZED DISTRIBUTORS OF , NALCO, JINDAL, THYSSENKRUPP, VIRGO, MANKASIA AND METENERE

Types of 3003 H14 Aluminium Plate Manufacturer in China

3003 H14 Aluminium Plate (3) 3003 H14 Aluminium Plate (2)

3003 H14 Aluminium Plates Product Range
Alloy No. Thickness
(mm)
Width
(mm)
Length
(mm)
Temper
3003 H14 Aluminium Plate 0.2-5.0 20-2200 20-8000 O, H12, H22, H14, H16, H18, H24, H26

 

Standard Specification of 3003 H14 Aluminium Plate

Standards and specifications by country

Specification Alloy Temper Company
Europe
AMS QQ-A-250/2 3003 O, H14  
European Standard BS (OLD) USA (AA) GERMANY (DIN) ISO IS Canadian
EN AW-3003 N3 3003 AlMnCu AlMn1Cu 31000 3 S

 

3003 H14 Aluminium Plate Sizes

Sizes (mm) Theoretical Mass KG/Plate
2000 X 1000 X 0.5 2500 X 1250 X 0.5
2000 X 1000 X 0.7 2500 X 1250 X 0.7
2000 X 1000 X 0.9 2500 X 1250 X 0.9
2000 X 1000 X 1.2 2500 X 1250 X 1.2
3000 X 1500 X 1.2 2000 X 1000 X 1.6
2500 X 1250 X 1.6 3000 X 1500 X 1.6
2000 X 1000 X 2.0 2500 X 1250 X 2.0
3000 X 1500 X 2.0 2500 X 1250 X 2.5
2.79 4.36
3.91 6.10
5.02 7.85
6.74 10.46
15.01 8.93
13.95 20.09
11.16 17.44
25.11 21.80

 

3003 H14 Aluminium Plate Weight Chart

Width: 1.000 mm | Length: 2.000 mm

dsadasdas

Product Thickness Weight
3003 H14 Aluminium Plate 0,30 mm 0,810 Kg/m2
3003 H14 Aluminium Plate 0,40 mm 1,080 Kg/m2
3003 H14 Aluminium Plate 0,50 mm 1,350 Kg/m2
3003 H14 Aluminium Plate 0,60 mm 1,620 Kg/m2
3003 H14 Aluminium Plate 0,70 mm 1,890 Kg/m2
3003 H14 Aluminium Plate 0,80 mm 2,160 Kg/m2
3003 H14 Aluminium Plate 0,90 mm 2,430 Kg/m2
3003 H14 Aluminium Plate 1,00 mm 2,700 Kg/m2
3003 H14 Aluminium Plate 1,20 mm 3,240 Kg/m2
3003 H14 Aluminium Plate 1,40 mm 3,780 Kg/m2
3003 H14 Aluminium Plate 1,50 mm 4,050 Kg/m2
3003 H14 Aluminium Plate 1,60 mm 4,320 Kg/m2
3003 H14 Aluminium Plate 1,80 mm 4,860 Kg/m2
3003 H14 Aluminium Plate 2,00 mm 5,400 Kg/m2
3003 H14 Aluminium Plate 2,20 mm 5,940 Kg/m2
3003 H14 Aluminium Plate 2,50 mm 6,750 Kg/m2
3003 H14 Aluminium Plate 3,00 mm 8,100 Kg/m2
3003 H14 Aluminium Plate 4,00 mm 10,800 Kg/m2
3003 H14 Aluminium Plate 5,00 mm 13,500 Kg/m2
3003 H14 Aluminium Plate 6,00 mm 16,200 Kg/m2
3003 H14 Aluminium Plate 10,00 mm 27,000 Kg/m2
3003 H14 Aluminium Plate 12,00 mm 32,400 Kg/m2
3003 H14 Aluminium Plate 15,00 mm 40,500 Kg/m2
3003 H14 Aluminium Plate 20,00 mm 54,000 Kg/m2

 

3003 H14 Aluminium Plate Chemical Composition

Alloy (ISS) Equivalent alloy (A.A) Copper Magnesium Silicon Iron Managanese Others* (Total) Remarks
Old New U.S.A Min. Max. Min. Max. Min. Max. Min. Max. Max Max. Aluminum 99.0% Min. 
3 31000 3003 0.1 0.1 0.6 0.7 0.8 1.5 0.4

Aluminium 3003 H14 Plate Mechanical Properties

Plate (according to the standard EN 485-2):

State
Specified thickness
Rm (MPa)
Rp0,2 (MPa)
A %
Bending radius
Hardness HBS
More than
until
mini
maxi
mini
maxi
A 50
A
180°
90°
F
>2,5
80,0
95
O/H111
0,20,51,53,06,0

12,5

0,51,53,06,012,5

50,0

9595959595

95

135135135135135

135

3535353535

35

1517202324

 

     

23

0 e0 e0 e1,0 e 

 

0 e0 e0 e1,0 e1,5 e

 

2828282828

28

H112
>6,012,5 12,580,0 115100
7040
10   18 3529
H12
0,20,51,53,06,0

12,5

0,51,53,06,012,5

40,0

120120120120120

120

160160160160160

160

9090909090

90

34567

 

     

8

1,5 e

1,5 e

1,5 e

 

 

 

0 e

0,5 e

1,0 e

1,0 e

2,0 e

 

3838383838

38

H14
0,20,51,53,06,0

12,5

0,51,53,06,012,5

25,0

145145145145145

145

185185185185185

185

125125125125125

125

   22345

 

 

 

 

 

 

5

2,0 e

2,0 e

2,0 e

 

 

 

0,5 e

1,0 e

1,0 e

2,0 e

2,5 e

 

4646464646

46

H16
0,20,51,5 0,51,54,0 170170170 210210210 150150150
122

2,5 e

2,5 e

2,5 e

1,0 e

1,5 e

2,0 e

545454
H18
0,20,51,5 0,51,53,0 190190190
170170170
122

1,5 e

2,5 e

3,0 e

606060
H19
0,20,51,5 0,51,53,0 210210210 180180180
122 656565
H22
0,20,51,53,06,0 0,51,53,06,012,5 120120120120120 160160160160160 8080808080
678911  

1,0 e

1,0 e

1,0 e

 

 

0 e0,5 e1,0 e1,0 e1,0 e 3737373737
H24
0,20,51,53,06,0 0,51,53,06,012,5 145145145145145 185185185185185 115115115115115
44568

1,5 e

1,5 e

1,5 e

 

 

0,5 e

1,0 e

1,0 e

2,0 e

2,5 e

4545454545
H26
0,20,51,5 0,51,54,0 170170170 210210210 140140140
233
2,0 e2,0 e2,0 e 1,0 e1,5 e2,0 e 535353
H28
0,20,51,5 0,51,53,0 190190190
160160160
223
1,5 e2,5 e3,0 e 595959
Alloy Designation UK
Specifications
US
Specifications
US Federal
Specifications
European
Specifications
Other
3003
A93003
  AMS 4006 3003-T0 Sheet, plate
AMS 4008 3003-H14 Sheet, plate
AMS 4067 3003-H14 Seamless tube
QQ-A-225/2 3003 Cold finished bar
QQ-A-250/2 3003 Sheet and plate
WW-T-700/2 3003 Seamless tube
   

Aluminum Alloy Heat Treatment Temper Designations

Basic Aluminum Heat Treatment Designations

  • F As Fabricated
  • O Annealed
  • H Strain Hardened
  • W Solution Heat Treated
  • T Solution Heat Treated

Heat Treating T Temper Codes for Aluminium 3003 H14 Plates

  • T1 – Cooled from an elevated temperature shaping process and naturally aged to a substantially stable condition.
  • T2 – Cooled from an elevated temperature shaping process, cold worked, and naturally aged to a substantially stable condition.
  • T3 – Solution heat treated, cold worked, and naturally aged to a substantially stable condition.
  • T4 – Solution heat treated, and naturally aged to a substantially stable condition.
  • T5 – Cooled from an elevated temperature shaping process then artificially aged.
  • T6 – Solution heat treated then artificially aged.
  • T7 – Solution heat treated then overaged/stabilized.
  • T8 – Solution heat treated, cold worked, then artificially aged.
  • T9 – Solution heat treated, artificially aged, then cold worked.
  • T10 – Cooled from an elevated temperature shaping process, cold worked, then artificially aged.

Additional digits may be used after the first T temper digit to indicate subsequent stress relieving by processes such as stretching, compressing, or a combination.

H Temper Strain Hardening Codes for Aluminium 3003 H14 Plates

  • H1 – Strain hardened only
  • H2 – Strain hardened and partially annealed
  • H3 – Strain hardened and stabilized
  • H4 – Strain hardened and lacquered or painted. This assumes that thermal affects from the coating process affect the strain hardening; seldom encountered.

3003 H14 Packing Information of Aluminum plate :

Application of 3003 H14 Aluminium Plate

3003 H14 Aluminium Plate is the most widely used form of Industrial Aluminium. 3003 H14 Aluminium Plates find applications in various industries such as manufacturing cans and packages, transportation, home appliances, building and construction.