5083 Aluminium Plate
Aluminium Alloy 5083 plate is known for exceptional performance in extreme environments. Aluminum 5083 Plateis highly resistant to attack by both seawater and industrial chemical environments. Alloy 5083 also retains exceptional strength after welding. 5083 Aluminum Plate has the highest strength of the non-heat treatable alloys but is not recommended for use in temperatures in excess of 65 °C.
Sasa Aluminium is the leading manufacturer and exporter of 5083 Aluminium Plate. Supplier of ASTM B209 5083 Aluminium Plate from 0.5mm to 5mm Thick 1000mm x 1000mm to 2500mm x 1250mm Tempers manufactured in accordance with international standards ASTM B209, ASTM-B-209, EN573, and EN485, check 5083 Aluminium Plate price. The general widths of 5083 H16 Aluminum Plates are 1000mm, 1250mm and 1500mm, while common lengths are 2000mm, 2500 mm and 3000mm respectively. Wholesale Trader of 5083 Commercial Aluminium Plate offered by Sasa Aluminium , China. Stockist of 5083 Aluminium Plate, H32 5083 Aluminium Stucco Plate, H38 Commercial 5083 Aluminium Plate, ASME SB209 5083 Aluminium Patterned Plate, 5083 Mill Finish, 5083 Aluminium Extruded Plate, 5083 Aluminium Plate and 5083 Aluminium Plate in China.
| Standard Dimensions of 5083 Aluminium Plate: |
| Aluminium Alloy | ASTM B209 5083 |
| Aluminium 5083 Plate Temper | O, H12, H14, H16, H18, H22, H24, H26, H32, H112 |
| Aluminium 5083 Plate Thickness | 0.5mm-150mm |
| Aluminium 5083 Plate Width | 500-2000mm |
| Aluminium 5083 Plate Length | to clients’ requirement |
| Aluminium 5083 Plate Coating | Polyester, Fluorocarbon, polyurethane and epoxy coating |
| 5083 Aluminium Plate Coating finish | PVDF, POLYESTER(PE) |
| Aluminium 5083 Plate Surface | Polished, hair line, brush, sand blast, checkered, embossed, etching, etc. Mill finish, Bright finish, paper interleaved, one side film, both sides film. |
| Aluminium 5083 Plate Gloss | Meet the customer requirement |
| Total coating thickness of Aluminium 5083 Plate | PVDF coating: More than 25 micron; Polyester coating: More than 18 micron |
| Aluminium 5083 Plate Coating hardness | (pencil hardness) more than 2H |
| Aluminium 5083 Plate Coating adhesive | No lower than1st grade |
| Aluminium 5083 Plate Impact resistance | No cracking or peeling (50kg/cm, ASTMD-2794: 1993) |
| Aluminium 5083 Plate Flexibility (T-bend) | 2T |
| Aluminium 5083 Plate MEK resistance | More than 10 |
| Available Aluminium 5083 Plate Stock Sizes | 1ft x 1ft, 1ft x 2ft, 1ft x 4ft, 2ft x 2ft, 2ft x 4ft, 4ft x 4ft, 4ft x 8ft, 4ft x 10ft or Cut to Size or Custom Shape. |
| Aluminium 5083 Plate Delivery Time | 30-60 days after receiving the prepayment |
| Aluminium 5083 Plate Packaging Details | Standard export package. One pallet is about 2-3 ton.Two steel belts in width and three in width. One 20GP container can load about 18-20 tons Aluminium 5083 Plate. One 40GP container can load about 24 tons Aluminium 5083 Plate |
| ASTM B209 Alloy 5083 Plate Outer packing | Export standard, wooden pallet |
| Bottom side Aluminium 5083 Plate is coated with protective polyester material, thickness more than 6 micron | |
| We Export Aluminium 5083 Plate to | Singapore, Indonesia, Ukraine, Korea, Thailand, Vietnam, Saudi Arabia, Brazil, Spain, Canada, USA, Egypt, Iran, China, Kuwait, Dubai, Oman, Kuwait, Peru, Mexico, Iraq, Russia, Malaysia, etc. |
| 5083 Aluminium Plate Products Show: |
| 5083 Aluminium Plates Product Range | ||||
|---|---|---|---|---|
| Alloy No. | Thickness (mm) |
Width (mm) |
Length (mm) |
Temper |
| 5083 Aluminium Plate | 0.2-5.0 | 20-2200 | 20-8000 | O, H12, H22, H14, H16, H18, H24, H26 |
| Standard Specification of 5083 Aluminium Plate: |
| Type of plate | Alloy designation | Temper | Mechanical properties | Availability (mm) |
|||||
|---|---|---|---|---|---|---|---|---|---|
| According to EN | According to DIN | According to PN | Chemical | Rm (min) (MPa) | Rp0,2 (MPa) |
Hardness (HB) |
|||
| Cast sawed mould plates (rough surface intended for machining) | ENAW 5083 | 3.3547 | PA13 | AlMg4,5Mn0,7 | Soft | 250 | 120 | 75 | Stock 20-300 |
| Cast sawed precision milled plates (machined surface, protective foil on the both-sides) | ENAW 5083 | 3.3547 | PA13 | AlMg4,5Mn0,7 | Soft | 250 | 120 | 75 | Stock 5-120 |
| Rolled plates (common rolled surface) | ENAW 5083 | 3.3547 | PA13 | AlMg4,5Mn0,7 | Soft | 250 | 120 | 75 | Stock 5-100 |
| 5083 Aluminium Plate Sizes: |
| Sizes (mm) | Theoretical Mass KG/Plate |
|---|---|
| 2000 X 1000 X 0.5 | 2500 X 1250 X 0.5 |
| 2000 X 1000 X 0.7 | 2500 X 1250 X 0.7 |
| 2000 X 1000 X 0.9 | 2500 X 1250 X 0.9 |
| 2000 X 1000 X 1.2 | 2500 X 1250 X 1.2 |
| 3000 X 1500 X 1.2 | 2000 X 1000 X 1.6 |
| 2500 X 1250 X 1.6 | 3000 X 1500 X 1.6 |
| 2000 X 1000 X 2.0 | 2500 X 1250 X 2.0 |
| 3000 X 1500 X 2.0 | 2500 X 1250 X 2.5 |
| 2.79 | 4.36 |
| 3.91 | 6.10 |
| 5.02 | 7.85 |
| 6.74 | 10.46 |
| 15.01 | 8.93 |
| 13.95 | 20.09 |
| 11.16 | 17.44 |
| 25.11 | 21.80 |
| 5083 Aluminium Plate Weight Chart: |
Width: 1.000 mm | Length: 2.000 mm
| Product | Thickness | Weight |
|---|---|---|
| 5083 Aluminium Plate | 0,30 mm | 0,810 Kg/m2 |
| 5083 Aluminium Plate | 0,40 mm | 1,080 Kg/m2 |
| 5083 Aluminium Plate | 0,50 mm | 1,350 Kg/m2 |
| 5083 Aluminium Plate | 0,60 mm | 1,620 Kg/m2 |
| 5083 Aluminium Plate | 0,70 mm | 1,890 Kg/m2 |
| 5083 Aluminium Plate | 0,80 mm | 2,160 Kg/m2 |
| 5083 Aluminium Plate | 0,90 mm | 2,430 Kg/m2 |
| 5083 Aluminium Plate | 1,00 mm | 2,700 Kg/m2 |
| 5083 Aluminium Plate | 1,20 mm | 3,240 Kg/m2 |
| 5083 Aluminium Plate | 1,40 mm | 3,780 Kg/m2 |
| 5083 Aluminium Plate | 1,50 mm | 4,050 Kg/m2 |
| 5083 Aluminium Plate | 1,60 mm | 4,320 Kg/m2 |
| 5083 Aluminium Plate | 1,80 mm | 4,860 Kg/m2 |
| 5083 Aluminium Plate | 2,00 mm | 5,400 Kg/m2 |
| 5083 Aluminium Plate | 2,20 mm | 5,940 Kg/m2 |
| 5083 Aluminium Plate | 2,50 mm | 6,750 Kg/m2 |
| 5083 Aluminium Plate | 3,00 mm | 8,100 Kg/m2 |
| 5083 Aluminium Plate | 4,00 mm | 10,800 Kg/m2 |
| 5083 Aluminium Plate | 5,00 mm | 13,500 Kg/m2 |
| 5083 Aluminium Plate | 6,00 mm | 16,200 Kg/m2 |
| 5083 Aluminium Plate | 10,00 mm | 27,000 Kg/m2 |
| 5083 Aluminium Plate | 12,00 mm | 32,400 Kg/m2 |
| 5083 Aluminium Plate | 15,00 mm | 40,500 Kg/m2 |
| 5083 Aluminium Plate | 20,00 mm | 54,000 Kg/m2 |
| 5083 Aluminium Plate Chemical Composition: |
| Alloy (ISS) | Equivalent alloy (A.A) | Copper | Magnesium | Silicon | Iron | Managanese Others* (Total) | Remarks | ||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Old | New | U.S.A | Min. | Max. | Min. | Max. | Min. | Max. | Min. | Max. | Max | Max. | Aluminum 99.0% Min. | ||
| N 8 | 54300 | 5083 | — | 0.1 | 4.0 | 4.9 | — | 0.4 | 0.7 | 0.5 | 1.0 | 0.4 | Chromium (0.15-0.35)Either Mn or Cr. shall be present. | ||
AS/NZS 1734 Aluminium and aluminium alloys – Flat sheet, coiled sheet and plate.
| Temper | 0.2% Proof Stress, MPa min † | Tensile Strength, MPa | Elongation % min ‡ |
|---|---|---|---|
| O (annealed) | 125 – 200 | 275 – 350 | 14 |
| H112 | 125 | 275 | 10 |
| H116 | 215 | 305 | 10 |
| H321 | 215 – 295 | 305 – 385 | 10 |
Aluminum Alloy Heat Treatment Temper Designations
Basic Aluminum Heat Treatment Designations
- F As Fabricated
- O Annealed
- H Strain Hardened
- W Solution Heat Treated
- T Solution Heat Treated
Heat Treating T Temper Codes for Aluminium 5083 Plates
- T1 – Cooled from an elevated temperature shaping process and naturally aged to a substantially stable condition.
- T2 – Cooled from an elevated temperature shaping process, cold worked, and naturally aged to a substantially stable condition.
- T3 – Solution heat treated, cold worked, and naturally aged to a substantially stable condition.
- T4 – Solution heat treated, and naturally aged to a substantially stable condition.
- T5 – Cooled from an elevated temperature shaping process then artificially aged.
- T6 – Solution heat treated then artificially aged.
- T7 – Solution heat treated then overaged/stabilized.
- T8 – Solution heat treated, cold worked, then artificially aged.
- T9 – Solution heat treated, artificially aged, then cold worked.
- T10 – Cooled from an elevated temperature shaping process, cold worked, then artificially aged.
Additional digits may be used after the first T temper digit to indicate subsequent stress relieving by processes such as stretching, compressing, or a combination.
H Temper Strain Hardening Codes for Aluminium 5083 Plates
- H1 – Strain hardened only
- H2 – Strain hardened and partially annealed
- H3 – Strain hardened and stabilized
- H4 – Strain hardened and lacquered or painted. This assumes that thermal affects from the coating process affect the strain hardening; seldom encountered.