6063 Aluminium Plate

Short Description:


  • Temper: O, H12, H14, H16, H18, H22
  • Thickness: 0.5mm-150mm
  • Width: 500-2000mm
  • Surface: Polished, hair line, brush, sand blast
  • Product Detail

    FAQ

    Product Tags

    Aluminum 6063 Plate offers medium strength and high corrosion resistance. With an aesthetically pleasing finish, the material is used in the fabrication of intricate extrusions used as finishing products. 6063 Aluminum Plate is supplied in the T6 temper (most common) but can also be supplied in T4, which has good formability.

    6063 (UNS A96063) is an aluminum plate that offers good extrudability and high quality surface. This alloy 6063 Plate is used for standard architectural shapes, custom solids and heatsinks. Aluminum Plate 6063 Also used for electrical applications in T5, T52 & T6 due to its electrical conductivity.

    Standard Dimensions of 6063 Aluminium Plate:

     

    Aluminium Alloy ASTM B209 6063
    Aluminium 6063 Plate Temper O, H12, H14, H16, H18, H22, H24, H26, H32, H112
    Aluminium 6063 Plate Thickness 0.5mm-150mm
    Aluminium 6063 Plate Width 500-2000mm
    Aluminium 6063 Plate Length to clients’ requirement
    Aluminium 6063 Plate Coating Polyester, Fluorocarbon, polyurethane and epoxy coating
    6063 Aluminium Plate Coating finish PVDF, POLYESTER(PE)
    Aluminium 6063 Plate Surface Polished, hair line, brush, sand blast, checkered, embossed, etching, etc.
    Mill finish, Bright finish, paper interleaved, one side film, both sides film.
    Aluminium 6063 Plate Gloss Meet the customer requirement
    Total coating thickness of Aluminium 6063 Plate PVDF coating: More than 25 micron; Polyester coating: More than 18 micron
    Aluminium 6063 Plate Coating hardness (pencil hardness) more than 2H
    Aluminium 6063 Plate Coating adhesive No lower than1st grade
    Aluminium 6063 Plate Impact resistance No cracking or peeling (50kg/cm, ASTMD-2794: 1993)
    Aluminium 6063 Plate Flexibility (T-bend) 2T
    Aluminium 6063 Plate MEK resistance More than 10
    Available Aluminium 6063 Plate Stock Sizes 1ft x 1ft, 1ft x 2ft, 1ft x 4ft, 2ft x 2ft, 2ft x 4ft, 4ft x 4ft, 4ft x 8ft, 4ft x 10ft or Cut to Size or Custom Shape.
    Aluminium 6063 Plate Delivery Time 30-60 days after receiving the prepayment
    Aluminium 6063 Plate Packaging Details Standard export package.
    One pallet is about 2-3 ton.Two steel belts in width and three in width.
    One 20GP container can load about 18-20 tons Aluminium 6063 Plate.
    One 40GP container can load about 24 tons Aluminium 6063 Plate
    ASTM B209 Alloy 6063 Plate Outer packing Export standard, wooden pallet
      Bottom side Aluminium 6063 Plate is coated with protective polyester material, thickness more than 6 micron
    We Export Aluminium 6063 Plate to Singapore, Indonesia, Ukraine, Korea, Thailand, Vietnam, Saudi Arabia, Brazil, Spain, Canada, USA, Egypt, Iran, China, Kuwait, Dubai, Oman, Kuwait, Peru, Mexico, Iraq, Russia, Malaysia, etc.

     

    Types of 6063 Aluminium Plate Manufacturer in China:

    6063 Aluminium Plate (3)     6063 Aluminium Plate (2)

    6063 Aluminium Plates Product Range
    Alloy No. Thickness
    (mm)
    Width
    (mm)
    Length
    (mm)
    Temper
    6063 Aluminium Plate 0.2-5.0 20-2200 20-8000 O, H12, H22, H14, H16, H18, H24, H26

     

    Standard Specification of 6063 Aluminium Plate:
    European Standard BS (OLD) USA (AA) GERMANY (DIN) ISO IS Canadian
    EN AW-6063 HE9 6063 AlMgSi0.5 AlMg0.7Si 63400 50S

     

    6063 Aluminium Plate Equivalent Grades:
    China
    U.S.A.
    BRITAIN
    CANADA GERMANY
    RUSSIA
    I.S.O.
    FRENCH
    New IS Old IS (A.A.)
    (B.S.)
      (DIN)
    63400 H9 6063 H9 50S Al-Mg-Si 0.5 Al-Si-1 Mg 6081

     

    6063 Aluminium Plate Sizes:
    Sizes (mm) Theoretical Mass KG/Plate
    2000 X 1000 X 0.5 2500 X 1250 X 0.5
    2000 X 1000 X 0.7 2500 X 1250 X 0.7
    2000 X 1000 X 0.9 2500 X 1250 X 0.9
    2000 X 1000 X 1.2 2500 X 1250 X 1.2
    3000 X 1500 X 1.2 2000 X 1000 X 1.6
    2500 X 1250 X 1.6 3000 X 1500 X 1.6
    2000 X 1000 X 2.0 2500 X 1250 X 2.0
    3000 X 1500 X 2.0 2500 X 1250 X 2.5
    2.79 4.36
    3.91 6.10
    5.02 7.85
    6.74 10.46
    15.01 8.93
    13.95 20.09
    11.16 17.44
    25.11 21.80

     

    6063 Aluminium Plate Weight Chart:

    Width: 1.000 mm | Length: 2.000 mm

    dsadasdas

    Product Thickness Weight
    6063 Aluminium Plate 0,30 mm 0,810 Kg/m2
    6063 Aluminium Plate 0,40 mm 1,080 Kg/m2
    6063 Aluminium Plate 0,50 mm 1,350 Kg/m2
    6063 Aluminium Plate 0,60 mm 1,620 Kg/m2
    6063 Aluminium Plate 0,70 mm 1,890 Kg/m2
    6063 Aluminium Plate 0,80 mm 2,160 Kg/m2
    6063 Aluminium Plate 0,90 mm 2,430 Kg/m2
    6063 Aluminium Plate 1,00 mm 2,700 Kg/m2
    6063 Aluminium Plate 1,20 mm 3,240 Kg/m2
    6063 Aluminium Plate 1,40 mm 3,780 Kg/m2
    6063 Aluminium Plate 1,50 mm 4,050 Kg/m2
    6063 Aluminium Plate 1,60 mm 4,320 Kg/m2
    6063 Aluminium Plate 1,80 mm 4,860 Kg/m2
    6063 Aluminium Plate 2,00 mm 5,400 Kg/m2
    6063 Aluminium Plate 2,20 mm 5,940 Kg/m2
    6063 Aluminium Plate 2,50 mm 6,750 Kg/m2
    6063 Aluminium Plate 3,00 mm 8,100 Kg/m2
    6063 Aluminium Plate 4,00 mm 10,800 Kg/m2
    6063 Aluminium Plate 5,00 mm 13,500 Kg/m2
    6063 Aluminium Plate 6,00 mm 16,200 Kg/m2
    6063 Aluminium Plate 10,00 mm 27,000 Kg/m2
    6063 Aluminium Plate 12,00 mm 32,400 Kg/m2
    6063 Aluminium Plate 15,00 mm 40,500 Kg/m2
    6063 Aluminium Plate 20,00 mm 54,000 Kg/m2

     

    6063 Aluminium Plate Chemical Composition:
    Alloy (ISS) Equivalent alloy (A.A) Copper Magnesium Silicon Iron Managanese Others* (Total) Remarks
    Old New U.S.A Min. Max. Min. Max. Min. Max. Min. Max. Max Max. Aluminum 99.0% Min. 
    H 9 63400 6063 0.1 0.4 0.9 0.3 0.7 0.6 0.3 0.4

     

    Aluminium 6063 Plate Mechanical Properties:
    Mechanical Properties
    Hardness, Brinell 73 73  AA; Typical; 500 g load; 10 mm ball
    Hardness, Knoop 96 96  Converted from Brinell Hardness Value
    Hardness, Vickers 83 83  Converted from Brinell Hardness Value
    Ultimate Tensile Strength 241 MPa 35000 psi  AA; Typical
    Tensile Yield Strength 214 MPa 31000 psi  AA; Typical
    Elongation at Break 12 % 12 %  AA; Typical; 1/16 in. (1.6 mm) Thickness
    Modulus of Elasticity 68.9 GPa 10000 ksi  AA; Typical; Average of tension and compression. Compression modulus is about 2% greater than tensile modulus.
    Ultimate Bearing Strength 434 MPa 62900 psi  Edge distance/pin diameter = 2.0
    Bearing Yield Strength 276 MPa 40000 psi  Edge distance/pin diameter = 2.0
    Poisson’s Ratio 0.33 0.33  
    Fatigue Strength 68.9 MPa 10000 psi  AA; 500,000,000 cycles completely reversed stress; RR Moore machine/specimen
    Machinability 50 % 50 %  0-100 Scale of Aluminum Alloys
    Shear Modulus 25.8 GPa 3740 ksi  
    Shear Strength 152 MPa 22000 psi  AA; Typical

     

    Alloy Designation UK
    Specifications
    US
    Specifications
    US Federal
    Specifications
    European
    Specifications
    Other
    6063 BS H9 Alloy 6063
    DTD 372B 6063
    AMS 4156 6063-T6 Extrusions QQ-A-200/9 6063
    MIL-P-25995
    ASTM B210
    ASTM B221
    ASTM B241
    ASTM B345
    ASTM B429
    ASTM B483
    ASTM B491
       

    Aluminum Alloy Heat Treatment Temper Designations

    Basic Aluminum Heat Treatment Designations

    • F As Fabricated
    • O Annealed
    • H Strain Hardened
    • W Solution Heat Treated
    • T Solution Heat Treated

    Heat Treating T Temper Codes for Aluminium 6063 Plates

    • T1 – Cooled from an elevated temperature shaping process and naturally aged to a substantially stable condition.
    • T2 – Cooled from an elevated temperature shaping process, cold worked, and naturally aged to a substantially stable condition.
    • T3 – Solution heat treated, cold worked, and naturally aged to a substantially stable condition.
    • T4 – Solution heat treated, and naturally aged to a substantially stable condition.
    • T5 – Cooled from an elevated temperature shaping process then artificially aged.
    • T6 – Solution heat treated then artificially aged.
    • T7 – Solution heat treated then overaged/stabilized.
    • T8 – Solution heat treated, cold worked, then artificially aged.
    • T9 – Solution heat treated, artificially aged, then cold worked.
    • T10 – Cooled from an elevated temperature shaping process, cold worked, then artificially aged.

    Additional digits may be used after the first T temper digit to indicate subsequent stress relieving by processes such as stretching, compressing, or a combination.

    H Temper Strain Hardening Codes for Aluminium 6063 Plates

    • H1 – Strain hardened only
    • H2 – Strain hardened and partially annealed
    • H3 – Strain hardened and stabilized
    • H4 – Strain hardened and lacquered or painted. This assumes that thermal affects from the coating process affect the strain hardening; seldom encountered.

    Application of 6063 Aluminium Plate

    6063 Aluminium Plate is the most widely used form of Industrial Aluminium. 6063 Aluminium Plates find applications in various industries such as manufacturing cans and packages, transportation, home appliances, building and construction.